您現(xiàn)在的位置: 醫(yī)學(xué)全在線 > 醫(yī)學(xué)論文 > 論文投稿 > 正文:醫(yī)學(xué)免費(fèi)論文:不同離子交換時(shí)間和溫度對白榴石增強(qiáng)陶瓷彎曲強(qiáng)度的影響
    

醫(yī)學(xué)免費(fèi)論文:不同離子交換時(shí)間和溫度對白榴石增強(qiáng)陶瓷彎曲強(qiáng)度的影響

來源:本站原創(chuàng) 更新:2013-9-30 論文投稿平臺(tái)

醫(yī)學(xué)免費(fèi)論文:不同離子交換時(shí)間和溫度對白榴石增強(qiáng)陶瓷彎曲強(qiáng)度的影響

【摘要】目的: 研究不同離子交換時(shí)間和溫度對白榴石增強(qiáng)陶瓷雙軸彎曲強(qiáng)度的影響,為臨床應(yīng)用提供參考. 方法: 試件的蠟型制作采用將融化的鑄造蠟灌注于機(jī)械加工模具內(nèi),制成厚度和直徑一致的蠟型. 厚度為2.0 mm,直徑為18 mm圓片,共90個(gè). 實(shí)驗(yàn)分組首先按照同一時(shí)間下不同溫度即離子交換溫度為400℃,450℃,500℃,離子交換時(shí)間為3 h,每組試件10個(gè). 然后在確定最佳離子交換溫度的基礎(chǔ)上以不同時(shí)間分組即交換時(shí)間為3,5,7,9,11 h,每組試件10個(gè). 以不做打磨、上釉和離子交換的為對照組,試件為10個(gè). 根據(jù)ASTM標(biāo)準(zhǔn) F39478.1991(美國材料實(shí)驗(yàn)協(xié)會(huì))測試試件的雙軸彎曲強(qiáng)度. 經(jīng)oneway ANOVA及KruskalWallis秩和檢驗(yàn)統(tǒng)計(jì)分析各實(shí)驗(yàn)組. 結(jié)果: 同一處理時(shí)間不同處理溫度下的雙軸彎曲強(qiáng)度經(jīng)統(tǒng)計(jì)分析可知有統(tǒng)計(jì)學(xué)差異(P<0.01). 同一處理溫度不同處理時(shí)間下的雙軸彎曲強(qiáng)度經(jīng)統(tǒng)計(jì)分析可知有統(tǒng)計(jì)學(xué)差異(P<0.01). 與對照組比較均存在統(tǒng)計(jì)學(xué)差異(P<0.01). 結(jié)論: cerinate熱壓鑄陶瓷的離子交換處理較佳的溫度為450℃,時(shí)間為11 h.

【關(guān)鍵詞】  牙瓷料;陶瓷;離子交換;雙軸彎曲強(qiáng)度

Effect of different time/temperature of ion exchange on the biaxial flexural strength of heat pressed ceramic

WANG Hui, CHEN JiHua,  SHI ChangXi, SHEN LiJuan

Department of Prosthodontics, College of Stomatology, Fourth Military Medical University, Xian 710033, China

【Abstract】 AIM: To study the effect of different time/temperature of ion exchange on the biaxial flexural strength of heat pressed ceramic. METHODS: Eighty disks of Cerinate ceramic specimens (shade 2), 18 mm in diameter and 2.0 mm thick, were prepared. The specimens were manufactured according to the companys recommendations. Ten disks were used as controls. The remaining disks were divided into 7 groups of 10 disks each and ionexchanged specimens were made by the treatment of potassium salt at 400℃, 450℃, 500℃ for 3 h and at the optimal temperature for 5, 7, 9, 11 h. The biaxial flexural strength was evaluated by a threepoint bending in a universal machine according to ASTM Standard (F39478.1991). RESULTS: The biaxial flexural strength had significant difference among different treatment temperature and time groups (P<0.01). Compared with control group, the biaxial flexural strength of each experimental group was also statistically significantly different (P<0.01).  CONCLUSION: The ionexchange process of the Cerinate hot pressed ceramic should be performed at 450℃ for 11 h.

【Keywords】 dental porcelain; porcelain; ionexchange; biaxial flexural strength醫(yī).學(xué).全.在.線52667788.cn

 0引言

隨著人們對牙科修復(fù)體的美觀要求的增加,越來越多的臨床醫(yī)生關(guān)注于陶瓷材料的美觀性和生物相容性,但由于陶瓷材料自身的缺點(diǎn)如脆性大、強(qiáng)度差. 作為牙科修復(fù)材料在燒結(jié)過程中在瓷表面形成張應(yīng)力和微裂紋,從而降低了陶瓷的強(qiáng)度,影響其在口腔復(fù)雜的化學(xué)環(huán)境下的使用壽命. 因此應(yīng)運(yùn)而生了陶瓷表面增強(qiáng)技術(shù),以減少和防止陶瓷表面微裂紋的產(chǎn)生和擴(kuò)散. 陶瓷表面增強(qiáng)技術(shù)的離子在陶瓷表面的擴(kuò)散率受交換的溫度和交換時(shí)間的影響,因此需要確定最佳的交換時(shí)間和溫度,使熱壓鑄陶瓷表面強(qiáng)度獲得最佳, 為臨床應(yīng)用提供依據(jù)和參考.


[1] [2] [3] [4] 下一頁

...
關(guān)于我們 - 聯(lián)系我們 -版權(quán)申明 -誠聘英才 - 網(wǎng)站地圖 - 網(wǎng)絡(luò)課程 - 幫助
醫(yī)學(xué)全在線 版權(quán)所有© CopyRight 2006-2046, MED126.COM, All Rights Reserved
浙ICP備12017320號
百度大聯(lián)盟認(rèn)證綠色會(huì)員實(shí)名網(wǎng)站 360認(rèn)證可信網(wǎng)站 中網(wǎng)驗(yàn)證